Only natural origin components are used for the manufacture of Magnesium Oxide boards, therefore it does not contain harmful and toxic substances and guarantees its absolute environmental friendliness and safety for human health.
MgO board MAGNECO PREMIUM is an eco-friendly, high-strength versatile material, widely used for internal and external finishing works. It is manufactured according to "The National Technical Assessment ITB-KOT-2017/0062 issue 2" and "Agrement Tehnic 001SC-04/902-2024".
Due to its physical and mechanical properties and operational qualities, such as strength, flexibility, fire and moisture resistance, MgO board is the best alternative to the most popular building and finishing materials.
In most cases, its use is more expedient than the use of gypsum drywall, any other gypsum-based materials, plywood, aquapanel boards, and plate materials such as chipboard, QSB, OSB, slate, fibre cement boards, etc.
Ukrainian-made MgO board MAGNECO PREMIUM is a sheet material with a thickness of 4 mm, 6 mm, 8 mm, 10 mm and 12 mm. We manufacture boards in various sizes depending on your needs: the width of our MgO board is 1200 mm, and the length can be anything up to and including 3050 mm.
The ability to produce the MgO board in the required size will reduce installation time and help minimize waste.
Main application areas of MgO board MAGNECO PREMIUM:
| ITEM | ESSENTIAL CHARACTERISTICS | VALUES | REPORT REFERENCE |
| 1 | Dimensions for thicknesses of 4-12 mm | 1200x2400-3050 | |
| 2 | Density, kg/m3 | 730...850 | PN-EN 12467+A2:2018 |
| 3 | Total water absorption, % boards with a thickness of 4-8 mm boards with a thickness of 10, 12 |
≤20 ≤28 |
PN-EN 520+A1:2012 |
| 4 | Flexural strength, MPa: boards with a thickness of 4- 8 mm boards with a thickness of 10, 12 |
≥10,0 ≥7,0 |
PN-EN 12467+A2:2018 |
| 5 | Flexural strength after soaking in water for 24 hours, MPa boards with a thickness of 4- 8 mm boards with a thickness of 10, 12 |
≥8,0 ≥5,0 |
|
| 6 | Hardness determined by the indentation diameter, mm |
≤15 | PN-EN 15283- 2+A1:2012 |
| 7 | Adhesion of fiberglass mesh to the surface of the board, MPa |
≥0,6 | PN-EN 311:2004 |
| 8 | Impact resistance with a hard body, mm/mm | ≥18 | PN-EN 1128:2000 |
| 9 | Compressive strength, MPa | ≥15 | PN-EN 826:2013 |
| 10 | Dimensional stability under specified temperature and humidity conditions: - Relative change in length with humidity change from 65 to 85% and from 65 to 30%, mm/m - Relative change in thickness with humidity change from 65 to 85% and from 65 to 30%, % |
≤1 ≤1 |
PN-EN 318:2004 |
| 11 | Shear strength, N | ≥750 | PN-EN 520+A1:2012 |
| 12 | Water vapor diffusion resistance coefficient, μ: - boards with a thickness of 4-8 and 10 mm - boards witha thickness of 12 |
11,0 ± 0,5 7,0 ± 0,5 |
PN-EN 12572:2016 |
| 13 | Diffusively equivalent air layer thickness, Sd, m | ≤0,1 | |
| 14 | Reaction to fire | A2-s1,d0 | PN-EN 13501- 1+A1:2010 |
| 15 | Thermal conductivity coefficient (declared value) W/(m*K) |
0,31 | PN-EN 12664:2022 PN-EN ISO 10456:2009 |
| 16 | Emission of volatile organic compounds (VOC) - time required to reach permissible concentrations of harmful substances for health, days |
≤28 | PN-EN ISO 16000- 9:2009 |